Oxidized Bitumen 90/10 Definition

Oxidized Bitumen 90/10 (in another word, oxidized Asphalt 90/10, blown bitumen 90/10) is Semi Solid grade of pure petroleum bitumen manufactured by air-blowing through an asphalt flux. Special physical properties of its grade can be used in different applications in the construction business. Oxidized asphalt 90/10 is based on petroleum bitumen which is made by oxidized asphalt 60/70 by hot air. The numbers relate to the midpoint of the material’s softening point and penetration respectively. The softening point value is the degrees Centigrade measured by the Ring and Ball method as determined by ASTM D36. The penetration value is in 1/10 mm as determined by IP49 or ASTM- D5.

Oxidized Bitumen 90/10 Applications

Oxidized Bitumen 90/10 uses in the chemical, fuel, lacquers, varnishes, paint paper-pulp-board, textile processing, road construction, pavement, civil works, roofing, construction industries; sealing and insulating buildings, adhesive, crack seal and repairmen, construction materials additive, dust-binding, insulating and impregnating agent, make rubber and plastic products. The asphalt 90/10 products are for paving. also used in asphalt-based paints for corrosion protection of metals, in lining public works structures, adhesives in electrical laminates, base for synthetic turf; typical uses for asphalt 90/10 used also for water-proof application and corrosion resistance for pipe coating, Portland cement pavement, hydraulic applications, paint manufacturing, caulking, mastics, and damp proofing. asphalt 90/10 is using insulation and isolation bitumen membrane sheet. Also, Car undercoating Automobile industry is specially required for Blown Asphalt. Vehicle undercoating material is based on Bitumen. Bitumen provides excellent waterproof, dust proof and noise proof for automobile undercoating.

20200512123159kf3f

 

Blown Asphalt 90/10 should be heated double temperature against the softening point to be able to have flow and viscosity. To use asphalt 90/10, surfaces must be dry, clean and free of loose particles, formwork, curing products, irregularities, slurry, etc.

Blown Asphalt 90/10 CHARACTERISTICS

CHARACTERISTIC Test method Unit Specification
Specific gravity @25/25 C ASTM D70 (Kg/m3) 1.05 approx.
Penetration @ 25°c ASTM  D5 mm/10 5/15
Softening point °c ASTM  D36 °C 85/95
Ductility @25 °c ASTM  D113 Cm 1.5min
Loss on heating(wt) % ASTM  D6 Wt. % 0.2 max
Flashpoint c ASTM D92 °C 250 min
Solubility is CS2(wt) % ASTM  D4 Wt. % 99.5 max
Spot test A.A.S.H.O.T102 Negative